J.W. Harris Blockade 2mm x 20 Stick Tube

$23.60

SKU: JWH BK220R1 Manufacturer Part #: BK220R1 Category:

Description

The Harris Blockage Phosphorus Tin Silicon Brazing Alloy is a proprietary phosphorus-tin-silicon alloy engineered as an inexpensive alternative to copper-copper and copper-brass alloys. It is self-fluxing on copper and its lower melting temperature makes it an excellent choice for brass connections. BLOCKADE flows rapidly but can be used to “cap” brazed joints.

Blockade’s® unique silicon addition offers significant advantages over phos/copper and silver/phos/copper, (BCuP), brazing alloys. Among the benefits are: bright alloy color during cooling that allows visual verification of a good braze joint, improved ductility over BCuP-2 alloy, reduced brazing temperature, and reduced material costs. It is often used with Stay-Silv® white brazing flux as a replacement for high silver alloys when brazing brass.

Specifications:

Diameter 2mm
BK220R1

Additional information

Brand

Harris
Diameter

1/32
Type

Brazing Alloy

Reviews

There are no reviews yet.

Be the first to review “J.W. Harris Blockade 2mm x 20 Stick Tube”

Your email address will not be published. Required fields are marked *

Related products

J.W. Harris Stay-Silv 5 Medium-Silver PhosCopper Brazing Alloy 1/8″ X 20″

J.W. Harris Stay-Silv 5 Medium-Silver PhosCopper Brazing Alloy 1/8″ X 20″



Quick Add

The Harris Stay-Silv 5 medium-silver PhosCopper brazing alloy is designed for copper to copper applications. It can also be used on copper to low zinc brass but this application requires use of Stay Silv white brazing flux.

Like many phosphorus/copper brazing filler metals Stay Silv 5 will flow rapidly when heated quickly to its liquidus. This allows penetration into tight clearance connections. With slower heating, the alloy melting range provides the ability to filler wider gaps.

Stay Silv 5 is often chosen as an economical alternative to higher silver content alloys for copper and brass applications.

Stay Silv 5 is not recommended for brazing steel or other ferrous base metals. In these applications the phosphorus content promote

 Specifications:

Package Size 25 lbs Package
Diameter 1/8″
5620R
STARTING AT
$0.00
Quick View
Quick Add

J.W. Harris Stay-Silv 2 Low-Silver PhosCopper Brazing Alloy 1/8″ X 20″

J.W. Harris Stay-Silv 2 Low-Silver PhosCopper Brazing Alloy 1/8″ X 20″



Quick Add

Stay Silv 2 brazing filler metal is a medium temperature range alloy for brazing copper, and copper to brass. The addition of silver provides an 1190°F solidus which widens the melting range compared to Harris 0. Stay Silv 2 is useful for applications with clearances of 0.002″

25# package size

2620F
STARTING AT
$0.00
Quick View
Quick Add

J.W. Harris Stay Brite 1/16″ X 1# Spool

J.W. Harris Stay Brite 1/16″ X 1# Spool



Quick Add

The important advantage of Stay-Brite® solders is the greater strength of the overall component. After joining, its lower working temperature eliminates the weakening of the base metals caused by annealment from high brazing heat. The result is a stronger, more economical joint.

 

Stay-Brite® silver bearing solders have the same excellent affinity as SafetySilv® alloys for bonding with most of the ferrous and nonferrous alloys (including stainless steel, nickel, copper, brass, etc.) It provides a considerably higher than necessary elongation for sound dissimilar metal joints and vibration applications.

 

Stay-Brite® alloys range in temperature from 430°F to 535°F. Stay-Brite® solder eliminates oxide scale formed from brazing heat. No nitrogen purge is required for HVAC/R tubes. They are cadmium free and nontoxic. Stay-Brite® is a eutectic alloy with a single melting point of 430°F (221°C).

Specifications:

Package Size

1 lb Spool

Diameter

1/16
SB31
STARTING AT
$65.16
Quick View
Quick Add

J.W. Harris Stay-Clean Flux

J.W. Harris Stay-Clean Flux

Stay-Clean Liquid Soldering Flux is an inorganic acid & salt type flux. It is formulated to be active at temperatures optimum for a range of solder compositions and is ideal for soldering a variety of base metals.

 

Stay Clean liquid effectively removes surface oxide and prevents oxide formation during soldering. Stay Clean can be used with most tin based solder compositions and is an excellent companion flux with Harris Stay Brite® and Stay Brite® #8. Stay Clean is an active soldering flux. It works well on copper and brass but is more frequently used on base metals that require a more aggressive flux, such as steel, nickel, and stainless steel, (it is not suitable for aluminum or magnesium).

 

Minimal pre-cleaning is required with Stay Clean Flux, but it is good practice to remove excess oil, grease, or other surface contaminants prior to fluxing and soldering.

 

Flux should be applied with a brush or other type applicator. Avoid getting excess flux inside tube or other connections.

Flux residue is corrosive and a post-solder flux removal procedure should be employed. Because of this it is not recommended for use in electrical or electronic applications.

SCLF
STARTING AT
$7.89
Quick View
Quick Add