J.W. Harris Stay-Silv 5 Medium-Silver PhosCopper Brazing Alloy 1/8″ X 20″

Contact us at leads@tollgas.com or via the live chat feature to get current pricing

SKU: JWH5620R Manufacturer Part #: 5620R Category: Brazing & Soldering

Description

The Harris Stay-Silv 5 medium-silver PhosCopper brazing alloy is designed for copper to copper applications. It can also be used on copper to low zinc brass but this application requires use of Stay Silv white brazing flux.

Like many phosphorus/copper brazing filler metals Stay Silv 5 will flow rapidly when heated quickly to its liquidus. This allows penetration into tight clearance connections. With slower heating, the alloy melting range provides the ability to filler wider gaps.

Stay Silv 5 is often chosen as an economical alternative to higher silver content alloys for copper and brass applications.

Stay Silv 5 is not recommended for brazing steel or other ferrous base metals. In these applications the phosphorus content promote

Specifications:

Package Size	25 lbs Package
Diameter	1/8″

5620R

Additional information

Package Size	1, 25

Reviews

There are no reviews yet.

Be the first to review “J.W. Harris Stay-Silv 5 Medium-Silver PhosCopper Brazing Alloy 1/8″ X 20″”

Related products

J.W. Harris Stay-Clean Flux

Stay-Clean Liquid Soldering Flux is an inorganic acid & salt type flux. It is formulated to be active at temperatures optimum for a range of solder compositions and is ideal for soldering a variety of base metals.

Stay Clean liquid effectively removes surface oxide and prevents oxide formation during soldering. Stay Clean can be used with most tin based solder compositions and is an excellent companion flux with Harris Stay Brite® and Stay Brite® #8. Stay Clean is an active soldering flux. It works well on copper and brass but is more frequently used on base metals that require a more aggressive flux, such as steel, nickel, and stainless steel, (it is not suitable for aluminum or magnesium).

Minimal pre-cleaning is required with Stay Clean Flux, but it is good practice to remove excess oil, grease, or other surface contaminants prior to fluxing and soldering.

Flux should be applied with a brush or other type applicator. Avoid getting excess flux inside tube or other connections.

Flux residue is corrosive and a post-solder flux removal procedure should be employed. Because of this it is not recommended for use in electrical or electronic applications.

SCLF

STARTING AT

$7.89

Quick View

Quick Add

J.W. Harris Solar Flux Type B 1# Can

Quick Add

Solar Flux is a complex chemical compound in the form of a very fine powder. Solar Flux is mixed with alcohol (methanol/methyl alcohol preferred) and brushed on the weld joint. It is formulated to shield the back of the weld joint from oxygen, dissipate heat and unwanted oxides, and to clean the surface of the metal. It will aid in the flow of filler metal over base metal and form a protective barrier to prevent re-oxidation and heat scale.

Type B for stainless steel, (except 309, 310), precipitation hardening steels, chrome-moly steels, other alloy steels with nickel content below 25%

Specifications:

Package Size

1 lb Can

S0FB01

STARTING AT

$88.00

Quick View

Quick Add

J. W. Harris Stay-Silv 5 Medium-Silver PhosCopper Brazing Alloy 1/8″ X 20″

Quick Add

Like many phosphorus/copper brazing filler metals Stay Silv 5 will flow rapidly when heated quickly to its liquidus. This allows penetration into tight clearance connections. With slower heating the alloy melting range provides the ability to filler wider gaps.

Stay Silv 5 is often chosen as an economical alternative to higher silver content alloys for copper and brass applications.

Stay Silv 5 is not recommended for brazing steel or other ferrous base metals. In these applications the phosphorus content promote

Specifications:

Package Size	14 Stick Tube
Diameter	1/8″

5620R1

STARTING AT

$0.00

Quick View

Quick Add

J.W. Harris Blockade 2mm x 20 Stick Tube

Quick Add

The Harris Blockage Phosphorus Tin Silicon Brazing Alloy is a proprietary phosphorus-tin-silicon alloy engineered as an inexpensive alternative to copper-copper and copper-brass alloys. It is self-fluxing on copper and its lower melting temperature makes it an excellent choice for brass connections. BLOCKADE flows rapidly but can be used to “cap” brazed joints.

Blockade’s® unique silicon addition offers significant advantages over phos/copper and silver/phos/copper, (BCuP), brazing alloys. Among the benefits are: bright alloy color during cooling that allows visual verification of a good braze joint, improved ductility over BCuP-2 alloy, reduced brazing temperature, and reduced material costs. It is often used with Stay-Silv® white brazing flux as a replacement for high silver alloys when brazing brass.

Specifications: