AlcoTec ER5356 Aluminum MIG Wire
AlcoTec ER5356 Aluminum MIG Wire
AlcoTec Almigweld is made of 5356 alloy that has magnesium, manganese, chromium and titanium as the principle alloying elements. Non-heat treatable wire with 1060 to 1175 deg F melting range is classified as a general-purpose type filler alloy.
Typical Applications
- Trade designation: ALMIGWELD and ALTIGWELD
- Non-Heat treatable
- Similar to AlSi5 (DIN)
- ISO designation: AlMg5Cr(A)
- Principle alloying elements: Magenesium, Maganese, Chromium, Titanium
- Applicable specifications: ANSI/AWS A5.10 (ER & R)
AlcoTec ER4047 .035 1# Spool Aluminum MIG Wire
AlcoTec ER4047 .035 1# Spool Aluminum MIG Wire
Alcotec Alloy 4047 was originally developed as a brazing alloy (BAlSi-4) OR (718) to take advantage of its low melting point and narrow freezing range. In addition, it has a higher silicon content than 4043, which provides for increased fluidity and reduced shrinkage. The alloy produces bright and almost smut free welds. Hot cracking is significantly reduced when 4047 is used as a filler alloy. The alloy may be used in applications of sustained elevated temperatures.
Typical Applications
- Trade designation: ALMIGWELD and ALTIGWELD
- Non-Heat treatable
- Similar to AlSi12 (Germany), BS N21 (United Kingdom)
- ISO designation: AlSi12
- Principle alloying elements: Silicon
- Applicable specifications: ANSI/AWS A5.10 (ER & R), AMS 4190
Weldmark ER4043 Aluminum TIG Rod 1# tube
Weldmark ER4043 Aluminum TIG Rod 1# tube
4043 is a general purpose type aluminum welding wire. It is one of the oldest and most widely used welding and brazing alloys. This aluminum alloy contains silicon additives, which result in improved fluidity (wetting action) of the weld pool and also produces a weld less sensitive to cracking. Its bright weld finish makes it a popular choice of welders. ER4043 can be used to weld various grades of aluminum.
| AWS Class: ER4043 | Certification: AWS A5.10/ A5.10M:1999 |
| Alloy: ER4043 | AWS/ASME SFA A5.10 |
AlcoTec ER4043 Aluminum MIG Wire
AlcoTec ER4043 Aluminum MIG Wire
J. W. Harris 5356 Aluminum TIG Rod 10# box
J. W. Harris 5356 Aluminum TIG Rod 10# box
0535630, 0535660, 0535650
Alcotec ER4043 Aluminum TIG Rod
Alcotec ER4043 Aluminum TIG Rod
Alloy 4043 is one of the oldest and most widely used welding and brazing alloys. Almigweld and altigweld 4043 can be classified as a general purpose type filler alloy. The silicon additions result in improved fluidity (wetting action) to make the alloy a preferred choice by welders. The alloy is less sensitive to weld cracking and produces brighter, almost smut free welds.
Typical Applications
Welding Filler Wire
Spray and Flame Metallizing Wire
General Information
- Trade designation: ALMIGWELD and ALTIGWELD
- Non-Heat treatable
- Similar to AlSi5 (Germany), BS N21 (United Kingdom)
- ISO designation: AlSi5
- Principle alloying elements: Silicon
- Applicable specifications: ANSI/AWS A5.10 (ER & R), AMS 4190
Alcotec ER5356 Aluminum TIG Rod
Alcotec ER5356 Aluminum TIG Rod
AlcoTec Almigweld Aluminum TIG Welding Rod of is made of 5356 alloy that has magnesium, manganese, chromium and titanium as the principle alloying elements. Non-heat treatable wire with 1060 to 1175 degree F melting range is classified as a general-purpose type filler alloy. Rod is used in a wide variety of applications as it has moderate high strength capabilities. It obtains white color when anodized and is associated with ER5356 class of rod.
Features:
- Trade Designation: Almigweld and Altigweld
- Non-Heat treatable
- Similar to AlMg5 (DIN)
- EN ISO designation AlMg5Cr(A)
- Principle alloying elements: Magnesium, Manganese, Chromium, Titanium
- Moderate high strength capabilities
- Applicable specification: ANSI/AWS A5.10 (ER & R)