J.W. Harris Stay Brite 1/16″ X 1# Spool
J.W. Harris Stay Brite 1/16″ X 1# Spool
The important advantage of Stay-Brite® solders is the greater strength of the overall component. After joining, its lower working temperature eliminates the weakening of the base metals caused by annealment from high brazing heat. The result is a stronger, more economical joint.
Stay-Brite® silver bearing solders have the same excellent affinity as SafetySilv® alloys for bonding with most of the ferrous and nonferrous alloys (including stainless steel, nickel, copper, brass, etc.) It provides a considerably higher than necessary elongation for sound dissimilar metal joints and vibration applications.
Stay-Brite® alloys range in temperature from 430°F to 535°F. Stay-Brite® solder eliminates oxide scale formed from brazing heat. No nitrogen purge is required for HVAC/R tubes. They are cadmium free and nontoxic. Stay-Brite® is a eutectic alloy with a single melting point of 430°F (221°C).
Specifications:
|
Package Size |
1 lb Spool |
|
Diameter |
1/16 |
J.W. Harris Stay Brite Solder Kit
J.W. Harris Stay Brite Solder Kit
The Stay Brite lead-free solder kit contains .5 oz of silver solder and .5 oz of Stay Clear flux. It is for use on all metals except aluminum. This low temperature solder is excellent for many HVAC connections.
J.W. Harris AlSolder 500 Aluminum Solder Kit
J.W. Harris AlSolder 500 Aluminum Solder Kit
The Harris Al-Solder 500 aluminum solder & flux kit for torch or iron is used all solder-able alloys to each other and to dissimilar metals. Also for zinc die-cast. Forms excellent, corrosion resistant joints on the tough to solder aluminum alloys. Also beneficial as a high temperature solder on most other metals. Not recommended for magnesium.
Forms excellent corrosion resistant joints on the tough-to-solder aluminum alloys. Joins all solder-able aluminum alloys to each other and to dissimilar metals, both ferrous and nonferrous. Also beneficial as a high temperature solder on most other metals.
Procedure:
- Clean the area to be soldered
- Apply Stay Clean aluminum flux
- If using an open flame, heat indirectly with the torch in motion (do not direct the torch on the flux)
- Heat until the flux becomes a nut brown color
- Apply the alloy
- Discontinue heat as soon as flow
- Allow to cool. Remove flux residue with wire brush and hot water
Features:
· Tensile strength – Up to 20,000 PSI
· Solidus – 391ºF
· Liquidus – 482ºF
· Good color match on aluminum and zinc die cast
Specifications:
|
Package Includes |
1.75 oz Al-solder 500 1 oz Stay-Clean Aluminum Flux |
|
|
|
J.W. Harris 50/50 Solder 1/8″ 1# Spool
J.W. Harris 50/50 Solder 1/8″ 1# Spool
The Harris 50/50 common lead-bearing solder With some exceptions, can be used to join copper and most copper alloys, lead, nickel alloys and steel. Tin-lead solders are not recommended for joints subject to high stress or vibration in the cooling industry due to lack of sufficient elongation properties. These solders are also available with rosin or acid core. Note: It is illegal to use lead solders in both public and private potable water systems.
CAUTION: Lead-bearing solders are not to be used in potable water systems.
Typical Application: A tin-lead alloy with a wide melting range. Used for automotive, radiator, general purpose soldering, electrical applications.
Specifications:
|
Diameter |
1/8″ |
J.W. Harris Stay-Silv 2 Low-Silver PhosCopper Brazing Alloy 1/8″ X 20″
J.W. Harris Stay-Silv 2 Low-Silver PhosCopper Brazing Alloy 1/8″ X 20″
Stay Silv 2 brazing filler metal is a medium temperature range alloy for brazing copper, and copper to brass. The addition of silver provides an 1190°F solidus which widens the melting range compared to Harris 0. Stay Silv 2 is useful for applications with clearances of 0.002″
25# package size