AlcoTec ER5356 Aluminum MIG Wire
AlcoTec ER5356 Aluminum MIG Wire
AlcoTec Almigweld is made of 5356 alloy that has magnesium, manganese, chromium and titanium as the principle alloying elements. Non-heat treatable wire with 1060 to 1175 deg F melting range is classified as a general-purpose type filler alloy.
Typical Applications
- Trade designation: ALMIGWELD and ALTIGWELD
- Non-Heat treatable
- Similar to AlSi5 (DIN)
- ISO designation: AlMg5Cr(A)
- Principle alloying elements: Magenesium, Maganese, Chromium, Titanium
- Applicable specifications: ANSI/AWS A5.10 (ER & R)
AlcoTec ER4047 .035 1# Spool Aluminum MIG Wire
AlcoTec ER4047 .035 1# Spool Aluminum MIG Wire
Alcotec Alloy 4047 was originally developed as a brazing alloy (BAlSi-4) OR (718) to take advantage of its low melting point and narrow freezing range. In addition, it has a higher silicon content than 4043, which provides for increased fluidity and reduced shrinkage. The alloy produces bright and almost smut free welds. Hot cracking is significantly reduced when 4047 is used as a filler alloy. The alloy may be used in applications of sustained elevated temperatures.
Typical Applications
- Trade designation: ALMIGWELD and ALTIGWELD
- Non-Heat treatable
- Similar to AlSi12 (Germany), BS N21 (United Kingdom)
- ISO designation: AlSi12
- Principle alloying elements: Silicon
- Applicable specifications: ANSI/AWS A5.10 (ER & R), AMS 4190
AlcoTec ER4043 Aluminum MIG Wire
AlcoTec ER4043 Aluminum MIG Wire
Tillman Winter Glove
Tillman Winter Glove
Features
- Rugged, bourbon brown, select Shoulder split leather Cowhide.
- Heavy duty pile lining for extra warmth.
- Includes a Gunn Cut with Keystone thumb for easy movement.
- Double stitching on forefinger provides extra strength.
Tillman Cut Resistant MIG Glove
Tillman Cut Resistant MIG Glove
ANSI A7 Cut Resistant MIG Glove
Tillman’s 1357 MIG glove is designed so that dexterity is not compromised and comfort is emphasized. Tillman searched for soft, pliable top grain and split Cowhide to provide that broken in feeling even with an ANSI A7 cut liner. With the 1357, the user has a great sense of feel and touch to effectively perform tasks and lay down incredible welds. The 1357 offers a seamless forefinger for a great feel on the MIG trigger to help laying down a precise weld.
Features
- ANSI A7 cut resistance is achieved with a Dupont™ Kevlar® lining for unbeatable cut resistance, dexterity and comfort.
- Long lasting top grain Cowhide palm and fingers is soft and pliable and provides excellent tactile performance you expect from Tillman.
- Flexible wing thumb allows greater movement for a great grip on the gun or a torch.
- Top grain seamless index finger provides a natural feel on the trigger.
- A comfortable glove for MIG welding and material handling.
- Sewn with DuPont™ Kevlar® for added strength and resistance to spark and spatter for a longer life of the glove.
- Offered in sizes M, L for other sizes contact leads@tollgas.com
Alcotec ER4043 Aluminum TIG Rod
Alcotec ER4043 Aluminum TIG Rod
Alloy 4043 is one of the oldest and most widely used welding and brazing alloys. Almigweld and altigweld 4043 can be classified as a general purpose type filler alloy. The silicon additions result in improved fluidity (wetting action) to make the alloy a preferred choice by welders. The alloy is less sensitive to weld cracking and produces brighter, almost smut free welds.
Typical Applications
Welding Filler Wire
Spray and Flame Metallizing Wire
General Information
- Trade designation: ALMIGWELD and ALTIGWELD
- Non-Heat treatable
- Similar to AlSi5 (Germany), BS N21 (United Kingdom)
- ISO designation: AlSi5
- Principle alloying elements: Silicon
- Applicable specifications: ANSI/AWS A5.10 (ER & R), AMS 4190
Alcotec ER5356 Aluminum TIG Rod
Alcotec ER5356 Aluminum TIG Rod
AlcoTec Almigweld Aluminum TIG Welding Rod of is made of 5356 alloy that has magnesium, manganese, chromium and titanium as the principle alloying elements. Non-heat treatable wire with 1060 to 1175 degree F melting range is classified as a general-purpose type filler alloy. Rod is used in a wide variety of applications as it has moderate high strength capabilities. It obtains white color when anodized and is associated with ER5356 class of rod.
Features:
- Trade Designation: Almigweld and Altigweld
- Non-Heat treatable
- Similar to AlMg5 (DIN)
- EN ISO designation AlMg5Cr(A)
- Principle alloying elements: Magnesium, Manganese, Chromium, Titanium
- Moderate high strength capabilities
- Applicable specification: ANSI/AWS A5.10 (ER & R)
Tillman Heavy Duty MIG Glove
Tillman Heavy Duty MIG Glove
Tillman Heavy Duty Pearl Top Grain Cowhide Unlined MIG Glove
Features
- Heavy duty pearl Top grain Cowhide, unlined.
- 4” cuff for added protection.
- Wing thumb, Seamless forefinger for comfort.
- Includes Lock stitching with DuPont™ Kevlar® thread for added strength.
Tillman Medium Weight MIG Glove
Tillman Medium Weight MIG Glove
Tillman Brown Top Grain Goatskin Fleece Lined MIG Glove
FEATURES
- A Top grain Goatskin palm for best feel, Cowhide split back resists heat.
- Fleece lined for added heat protection without the bulk.
- Straight thumb for best gun grip.
- Thumb strap reinforcement for extra strength.
- Elastic back for snug fit.
- 3-1/2 in cuff for added protection.
- Sewn with Kevlar® stitching to protect seams.
Tillman TrueFit Deerskin Work Glove
Tillman TrueFit Deerskin Work Glove
Tillman Blue/Gold Top Grain Deerskin Leather Palm Mechanics Glove
Features
- Top grain gold Deerskin construction for all day comfort and protection
- Leather and spandex design will outlast and outperform all-synthetic high dexterity gloves
- Rough side out double palm for longer life and better gripping power
- Reinforced thumb to protect severe stress areas
- Smooth surface fingers for improved handling
- Elastic cuff with hook and loop closure provides secure fit, less bulk
- Top grain leather side bolsters add additional protection for side surface work
- All finger tips covered in leather for heavy wear area protection
- Not designed for welding